Aluminum silicon carbide carbon brick
AlSiC-Brick
Aluminum silicon carbide carbon brick, also known as ASC brick, uses fused corundum (or sintered corundum, super bauxite clinker), graphite and silicon carbide containing fixed carbon above 90%-95% as the main raw materials, and is combined with resin. It is formed by machine pressing after being kneaded by a kneader, and after drying, it is processed at a low temperature of 210°C.
Quantity
Aluminum silicon carbide carbon brick
Aluminum silicon carbide carbon brick, also known as ASC brick, uses fused corundum (or sintered corundum, super bauxite clinker), graphite and silicon carbide containing fixed carbon above 90%-95% as the main raw materials, and is combined with resin. It is formed by machine pressing after being kneaded by a kneader, and after drying, it is processed at a low temperature of 210°C.
Applications:
Mainly used for molten iron containing equipment in the iron and steel industry, such as torpedo tanks, molten iron tanks, mixing furnaces and other molten iron pretreatment equipment.
The main parameters
Keywords: refractory material, refractory brick, aluminum silicon carbide brick
Aluminum silicon carbide carbon brick, also known as ASC brick, uses fused corundum (or sintered corundum, super bauxite clinker), graphite and silicon carbide containing fixed carbon above 90%-95% as the main raw materials, and is combined with resin. It is formed by machine pressing after being kneaded by a kneader, and after drying, it is processed at a low temperature of 210°C.
Applications:
Mainly used for molten iron containing equipment in the iron and steel industry, such as torpedo tanks, molten iron tanks, mixing furnaces and other molten iron pretreatment equipment.
The main parameters
| Item | Specified value | ||
| ASC-Z | ASC-T | ASC-D | |
| W(Al2O3) % | 55 | 57 | 62 |
| W(SiC+FC) % | 17 | 14 | 10 |
| W(F.C)% | 8 | 6 | 4 |
| Apparent porosity % | 8 | 10 | 10 |
| Bulk density g/cm3 | 2.75 | 2.75 | 2.75 |
| Compressive strength MPa | 35 | 40 | 45 |
| High temperature flexural strength MPa （1400℃x0.5h） | 5 | 5.5 | 6 |
Keywords: refractory material, refractory brick, aluminum silicon carbide brick